According to API RP 571, under Caustic Stress Corrosion Cracking (Caustic Embrittlement):

“Cracking occurs in stressed components exposed to caustic (e.g., sodium hydroxide).”

“The most effective mitigation strategy is postweld heat treatment (PWHT), which relieves residual stress that promotes cracking.”

“Upgrading materials or controlling concentration may help, but do not replace stress relief.”

(Reference: API RP 571, Section 4.2.2.3 – Caustic SCC)

Thus, PWHT is the most effective prevention technique, making option A correct.

API RP 571 identifies these parameters as critical to the corrosion rate of carbon and low alloy steels in sour water environments:

“The extent of corrosion in sour water is influenced by pH, H₂S content, temperature, liquid velocity, and oxygen contamination.”

“These factors control the formation and stability of protective iron sulfide layers.”

(Reference: API RP 571, Section 4.3.2.1 – Sour Water Corrosion)

Therefore, the correct answer is A.

Comprehensive and Detailed Explanation From Exact Extract:

Per API RP 571, sulfidation corrosion rates are significantly accelerated by the presence of hydrogen. Hydrogen promotes:

Breakdown of protective sulfide scales

Increased diffusion of sulfur into the metal

Higher metal loss rates

This phenomenon is often referred to as hydrogen-assisted sulfidation and is commonly observed in refinery process units.

Moisture is more closely associated with oxidation mechanisms rather than high-temperature sulfidation.

Referenced Documents (Study Basis):

API RP 571 – Section on Sulfidation and High-Temperature Corrosion

According to API RP 571:

“Oxidation is the reaction of metal and oxygen to form oxides. It generally occurs in high temperature environments with excess oxygen.”

“Sulfidation is a high temperature corrosion mechanism that occurs due to interaction between sulfur-containing compounds and metal surfaces, forming metal sulfides. Like oxidation, sulfidation occurs in environments above 500 °F (260 °C).”

“Both oxidation and sulfidation can occur concurrently, particularly in mixed environments of oxygen and sulfur.”

(Reference: API RP 571, Sections 5.1.1 and 5.1.3 – Oxidation & Sulfidation)

These two mechanisms are thermally activated and occur in elevated temperature conditions found in heaters, furnaces, and piping systems. Hence, option B is correct.