API RP 571 – Hydrogen Stress Cracking – HF Acid Service:
“HF acid environments can cause hydrogen stress cracking (HSC) in carbon steel, particularly in areas with high hardness or residual stress.”
“This is distinct from general corrosion and requires specific inspection focus.”
So, option A is correct.