API RP 571 – Hydrogen Stress Cracking – HF Acid Service:

“HF acid environments can cause hydrogen stress cracking (HSC) in carbon steel, particularly in areas with high hardness or residual stress.”

“This is distinct from general corrosion and requires specific inspection focus.”

So, option A is correct.

According to API RP 571, high-cycle fatigue (HCF) is characterized by very tight, narrow cracks that can escape detection using typical NDE methods due to their minimal opening displacement and fine geometry.

From API RP 571 Section 5.2.1 (Fatigue - High Cycle):

"The cracks are usually tight and may be difficult to detect using conventional NDE techniques such as PT or MT. UT and RT may also have difficulty identifying these small, tight flaws, especially in early stages of propagation."

The primary issue in NDE is not the geometry (such as 90° corners) or ID location, but rather the tightness and early-stage subtlety of the cracks which results in reduced detectability. Therefore, option B is correct as it aligns most accurately with API RP 571's detailed characterization of HCF detection challenges.

API RP 571 notes in the context of Hydrochloric Acid Corrosion in overhead condensers:

“Titanium is highly resistant to low pH acidic aqueous phases, including hydrochloric acid formed during condensation in overhead systems.”

“Stainless steels like 316 and 410 are not suitable in the presence of free chlorides at low pH and elevated temperatures.”

(Reference: API RP 571, Section 4.3.3.3 – Hydrochloric Acid Corrosion)

Thus, Titanium is the preferred alloy under the described acidic and high-temperature conditions, making option B correct.