According to API RP 571 Section 5.2.1 (Fatigue – High Cycle and Low Cycle):
“Unsupported small-bore attachments like vents and drains are prone to high-cycle mechanical fatigue due to vibration. These attachments experience cyclic stress, especially near welds or bends.”
Thermal overload is unlikely without over-temperature data.
SSC (Option C) requires a wet H2S environment, which is not indicated.
Weld defects may contribute but are less likely the root cause without other signs.
Hence, mechanical fatigue (Option A) is most probable in this configuration.